RTO Exhaust Gas Purification and Gas Oxidation
RTO Exhaust Gas Purification and Gas Oxidation--Combined Plate Honeycomb Ceramic Regenerator for Metallurgical
Category: Heat storage Ceramic
Tag：RTO Exhaust Gas PurificationRTO Exhaust Gas Oxidation
Hit: 84
RTO Exhaust Gas Purification,RTO Exhaust Gas Oxidation
RTO Exhaust Gas Purification and Gas Oxidation--Combined Plate Honeycomb Ceramic Regenerator for Metallurgical Machinery
Details
The combined plate honeycomb ceramic heat storage body is composed of layers of 100 long × 100 wide × 6.8-11.6 thick toothed ceramic sheets, which are then bonded with high-temperature ceramic glue to form a large honeycomb ceramic of 305 × 305 × 101. The material is generally silicon-aluminum porcelain. It has the advantages of large heat storage, acid and alkali corrosion resistance, not easy to be contaminated by dust and oil, and low price. It is widely used in RTO and RCO devices for exhaust gas purification and gas oxidation.
Chemical Composition
Chemical Content | SiO₂ | Al₂O₃ | Fe₂O₃ | K₂O+Na₂O |
Content ( % ) | 67~76 | 16~25 | ≤1.5 | ≤4 |
Physical Properties
型号Sizes | ZHFW-S | ZHFW-125-1 | ZHFW-125 | ZHFW-160 | ZHFW-180 | ZHFW-200 |
| 2.2~2.4 | 2.2~2.4 | 2.2~2.4 | 2.2~2.4 | 2.2~2.4 | 2.2~2.4 |
| 1000~1180 | 730~830 | 800~930 | 850～1000 | 1000～1150 | 1050~1200 |
| ≥98 | ≥98 | ≥98 | ≥98 | ≥98 | ≥98 |
| <0.5 | <0.5 | <0.5 | <0.5 | <0.5 | <0.5 |
| 54 | 69 | 69 | 61 | 56 | 51 |
| 1200 | 1200 | 1200 | 1200 | 1200 | 1200 |
Specific Heat Capacity | 1070 | 670 | 670 | 810 | 940 | 1070 |
Thermal Conductivity | 1.5~2.0 | 1.5~2.0 | 1.5~2.0 | 1.5~2.0 | 1.5~2.0 | 1.5~2.0 |
Thermal Shock | 400 | 400 | 400 | 400 | 400 | 400 |
Axial | ≥0.6 | ≥0.4 | ≥0.4 | ≥0.5 | ≥0.6 | ≥0.7 |
Specifications and Sizes
Sizes | ZHFW-S | ZHFW-125-1 | ZHFW-125 | ZHFW-160 | ZHFW-180 | ZHFW-200 |
General Specifications(mm) | 305×305×101(101×101×101) | |||||
Inch Size (inch) | 12×12×4(4×4×4) | |||||
Specific Surface Area (m²/m³)(ft²/t³) | 722/220 | 410/125 | 410/125 | 525/160 | 590/180 | 655/200 |